Hydrogen Storage in the Dehydrated Prussian Blue Analogues M 3 [Co(CN) 6 ] 2 (M = Mn, Fe, Co, Ni, Cu, Zn)

The porosity and hydrogen storage properties for the dehydrated Prussian blue analogues M3[Co(CN)6]2 (M = Mn, Fe, Co, Ni, Cu, Zn) are reported. Argon sorption isotherms measured at 87 K afford BET surface areas ranging from 560 m2/g for Ni3[Co(CN)6]2 to 870 m2/g for Mn3[Co(CN)6]2; the latter value is comparable to the highest surface area reported for any known zeolite. All six compounds show significant hydrogen sorption at 77 K and 890 Torr, varying from 1.4 wt % and 0.018 kg H2/L for Zn3[Co(CN)6]2 to 1.8 wt % and 0.025 kg H2/L for Cu3[Co(CN)6]2. Fits to the sorption data employing the Langmuir-Freundlich equation give maximum uptake quantities, resulting in a predicted storage capacity of 2.1 wt % and 0.029…