Enhanced interfacial polarization loss induced by hollow engineering of hollow alloyed CoFe-ZIF nanocages/carbon nanofibers for efficient microwave absorption
Chengdu University of Information Technology · Chengdu University of Technology · +1 more institution
Indexed incrossref
Abstract
Hollow alloyed CoFe-ZIF/CNF composite fibers were successfully synthesized. The carbon fiber with dielectric loss wraps hollow alloyed CoFe-ZIF nanocages with magnetic loss to form a bamboo-shaped composite fiber to achieve magnetoelectric synergy.
Citation impact
60
total citations
- FWCI
- 20.28
- Percentile
- 100%
- References
- 63
Citations per year
Authors
6- DWDan Wu
Chengdu University of Information Technology, Chengdu University of Technology, Hubei University of Automotive Technology
- CFCong-Min FanCorresponding
Chengdu University of Information Technology, Chengdu University of Technology
- WLWusi LuoCorresponding
Hubei University of Automotive Technology
- YJYingzhi Jin
Chengdu University of Information Technology, Chengdu University of Technology
- QHQinchuan He
Chengdu University of Information Technology, Chengdu University of Technology
Topics & keywords
Topics
Keywords
- Nanocages
- Materials science
- Microwave
- Polarization (electrochemistry)
- Absorption (acoustics)
- Chemical engineering
- Nanofiber
- Carbon nanofiber
No related works found for this paper.